FAILURE ANALYSIS & MODELLING LABS

Fracture and Fatigue

-----------------------------------------------------------------------------------------------------

There are many modes of fracture. First and foremost any fractured surface must be preserved to save any evidence of the cause of fracture.

Two main causes of fracture of metals can occur by over stressing or fatigue.  Each type of fracture has distinct features that can help an experienced and knowledgeable failure analystto identify the root cause of failure.

Overload of a socket head cap screw caused by a sharp radius under head.

Fatigue Crack of a carbon steel pin with Beach marks from origin.

Materials

Two main causes of fracture of metals can occur by over stressing or fatigue.  Each type of fracture has distinct features that can help an experienced and knowledgeable failure analystto identify the root cause of failure.

Overload of a socket head cap screw caused by a sharp radius under head.

Fatigue Crack of a carbon steel pin with Beach marks from origin.

Services

Two main causes of fracture of metals can occur by over stressing or fatigue.  Each type of fracture has distinct features that can help an experienced and knowledgeable failure analystto identify the root cause of failure.

Overload of a socket head cap screw caused by a sharp radius under head.

Fatigue Crack of a carbon steel pin with Beach marks from origin.

Codes, Standards & Specifications

Two main causes of fracture of metals can occur by over stressing or fatigue.  Each type of fracture has distinct features that can help an experienced and knowledgeable failure analystto identify the root cause of failure.

Overload of a socket head cap screw caused by a sharp radius under head.

Fatigue Crack of a carbon steel pin with Beach marks from origin.